Scanning Magnetron Sputtered TiN Films Characterisation and Properties
Abstract: scanning magnetron target (274mmx174mm) is used to deposit tin film on to si ( p type 10 ohm cm resistivity) substrate for microelectronic application. To deposit best quality tin films with low resistivity 1 parametres. Such as deposition rate, scanning speed, target substrate distance (T. S. D) and ion current ma, Nitrogen partial pressure, were optimizd. Total nitrogen and argon pressure was kept at 5x10-3m bar. Tin films were sputter depositedon to si with different substrate bias. CU film is sputter deposited on to as deposited tin film since it is found as best substitute for diffusion barrier. Thickness of the TIN film is determined keeping in consideration diffusion length 2 of cu in tin at different temperature. Stylus dektak is used to obtain desired thickness of tin and copper films. cu/tin/si structure thus formed were annealed at different temperature to study microelectronic application for diffusion barrier. Resistivity fig1 of the cu/tin/si structure were obtained using four probe method, low resistivity cu/tin/si structure were preferred. Inter difussion of silicon and or top metal through the tin film was investigated. XRD fig 4 SEM fig5 EDAXfig6 of CU/tin/si obtained to determine its feasibility for micro electronic application.
Keywords: difussion, resistivity
Edition: Volume 8 Issue 12, December 2019,
Pages: 427 - 431
Similar Articles with Keyword 'resistivity'
Research Paper, Physics Science, India, Volume 5 Issue 6, June 2016Pages: 1160 - 1162
Structural Study of Fe/Al MLS as a Function of Fe Film Thickness
Research Paper, Physics Science, India, Volume 3 Issue 12, December 2014Pages: 2602 - 2608
Growth, Optical, Mechanical and Dielectric Properties of Potassium Tetraborate Tetrahydrate Single Crystal
S. Sathiskumar | T. Balakrishnan | K. Ramamurthi