Physical Properties of Geopolymer Concrete Incorporating Silica Fume and Ground Granulated Blast-Furnace Slag
Abstract: This research presents new matrixes geo-polymer concrete, cementing mainly on engineering properties discusses the physical properties. In addition, the study of polymer concrete on two productions. GEO-polymer concrete GGBS and SF was created. Alkaline solution were used in this study. They are sodium hydroxide, sodium silicate solution and superplasticizer.150 mm x 150 mm x 150 mm sample cube with a size of compressive strength were put to the test. GGBS concrete compressive strength of geo-polymer age 7, 14 and 28 days were 54.17, 66 and 69 on the MPa. And compressive strength of polymer concrete SF ground tests at the age of 7, 14 and 28 days were 1.45 1.42 1.45, and the MPa. GGBS concrete geo-polymer curing time at all compressive strength showed improved results. But geopolymer concrete compressive strength of SF given. In addition, 7 and 28 days old, low permeability and GGBS was made of geopolymer concrete were tested when absorption shown.
Keywords: Geopolymer Concrete, Silica Fume, Ground Granulated Blast, Furnace Slag
Edition: Volume 4 Issue 4, April 2015,
Pages: 2415 - 2419
Similar Articles with Keyword 'Geopolymer Concrete'
Downloads: 7 | Weekly Hits: ⮙1 | Monthly Hits: ⮙1
Experimental Result Paper, Civil Engineering, India, Volume 11 Issue 7, July 2022Pages: 804 - 810
Performance Evaluation of GGBFS and Rice Husk Ash based on Concrete Blocks
Dr. Sneha Gupta | Saurabh Kumar  | Desh Deepak Kumar
M.Tech / M.E / PhD Thesis, Civil Engineering, India, Volume 6 Issue 6, June 2017Pages: 1539 - 1560
Development of Fly Ash based Geopolymer Concrete
Tariq Ahmad Dar